Sacrificial coating and indirect printing apparatus employing sacrificial coating on intermediate transfer member

ABSTRACT

A sacrificial coating on an intermediate transfer member of an aqueous ink imaging system is disclosed. The sacrificial coating is made from ingredients comprising: a waxy starch; at least one polycarboxylic acid cross-linking agent; at least one hygroscopic material; and at least one surfactant.

DETAILED DESCRIPTION

Field of the Disclosure

This disclosure relates generally to indirect inkjet printers, and inparticular, to a sacrificial coating employed on an intermediatetransfer member of an inkjet printer.

Background

In aqueous ink indirect printing, an aqueous ink is jetted on to anintermediate imaging surface, which can be in the form of a blanket. Theink is partially dried on the blanket prior to transfixing the image toa media substrate, such as a sheet of paper. To ensure excellent printquality it is desirable that the ink drops jetted onto the blanketspread and become well-coalesced prior to drying. Otherwise, the inkimages appear grainy and have deletions. Lack of spreading can alsocause failing inkjet ejectors to be much more apparent, producingbroader streaks in the ink image. Spreading of aqueous ink isfacilitated by materials having a high surface energy.

However, in order to facilitate transfer of the ink image from theblanket to the media substrate after the ink is dried on theintermediate imaging surface, a blanket having a surface with arelatively low surface energy is preferred. Rather than providing thedesired spreading of ink, low surface energy materials tend to promote“beading” of individual ink drops on the image receiving surface.

Thus, an optimum blanket for an indirect image transfer process musttackle both the challenges of wet image quality, including desiredspreading and coalescing of the wet ink; and the image transfer of thedried ink. The first challenge—wet image quality—prefers a high surfaceenergy blanket that causes the aqueous ink to spread and wet thesurface. The second challenge—image transfer—prefers a low surfaceenergy blanket so that the ink, once partially dried, has minimalattraction to the blanket surface and can be transferred to the mediasubstrate.

Various approaches have been investigated to provide a solution thatbalances the above challenges. These approaches include blanket materialselection, ink design and auxiliary fluid methods. With respect tomaterial selection, materials that are known to provide optimum releaseproperties include the classes of silicone, fluorosilicone, afluoropolymer, such as TEFLON or VITON, and certain hybrid materials.These materials have low surface energy, but provide poor wetting.Alternatively, polyurethane and polyimide have been used to improvewetting, but at the cost of ink release properties. Tuning inkcompositions to address these challenges has proven to be very difficultsince the primary performance attribute of the ink is the performance inthe print head. For instance, if the ink surface tension is too high itmay not jet properly, depending on type of printheads, and it if is toolow it may drool out of the face plate of the printhead.

In addition to affecting image quality and transfer characteristics ofthe ink, the sacrificial coating properties can also affect waterfastness of the prints. Water fastness is a known concern for aqueousinks generally. Poor water fastness can result in smudging, reducedimage quality and unwanted transfer of ink such as to the fingers ofusers handling the images.

Identifying and developing new polymer coating materials that providegood wet image quality and/or image transfer with improved waterfastness would be considered a welcome advance in the art.

SUMMARY

An embodiment of the present disclosure is directed to a sacrificialcoating on an intermediate transfer member of an aqueous ink imagingsystem. The sacrificial coating is made from ingredients comprising: awaxy starch; at least one polycarboxylic acid cross-linking agent; atleast one hygroscopic material; and at least one surfactant.

Another embodiment of the present disclosure is directed to a wetsacrificial coating composition. The coating composition is made fromingredients comprising: a waxy starch; at least one polycarboxylic acidcross-linking agent; at least one hygroscopic material; at least onesurfactant; and a liquid carrier.

Yet another embodiment of the present disclosure is directed to anindirect printing process. The process comprises providing an inkcomposition to an inkjet printing apparatus comprising an intermediatetransfer member. A wet sacrificial coating composition is deposited ontothe intermediate transfer member. The wet sacrificial coatingcomposition is made from ingredients comprising: a waxy starch; at leastone polycarboxylic acid cross-linking agent; at least one hygroscopicmaterial; at least one surfactant; and a liquid carrier. The wetsacrificial coating composition is dried to form a sacrificial coating.Droplets of ink are ejected in an imagewise pattern onto the sacrificialcoating. The ink is at least partially dried to form a substantially dryink pattern on the intermediate transfer member. Both the substantiallydry ink pattern and the sacrificial coating are transferred from theintermediate transfer member to a final substrate.

The sacrificial coating compositions of the present disclosure canprovide one or more of the following advantages: coatings having goodwettability, coatings having good ink wetting and ink spreading, imagetransfer member coatings exhibiting improved wet image quality and/orimproved image transfer with aqueous inks, improved physical robustnessor increased shelf life, improved image quality; or improved waterfastness.

It is to be understood that both the foregoing general description andthe following detailed description are exemplary and explanatory onlyand are not restrictive of the present teachings, as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated in and constitute apart of this specification, illustrate embodiments of the presentteachings and together with the description, serve to explain theprinciples of the present teachings.

FIG. 1 is a schematic drawing of an aqueous indirect inkjet printer thatprints sheet media, according to an embodiment of the presentdisclosure.

FIG. 2 is a schematic drawing of a surface maintenance unit that appliesa hydrophilic sacrificial coating composition to a surface of anintermediate transfer member in an inkjet printer, according to anembodiment of the present disclosure.

FIG. 3 is a block diagram of a process for printing images with anindirect inkjet printer that uses aqueous inks, according to anembodiment of the present disclosure.

FIG. 4A is a side view of a hydrophilic sacrificial coating compositionthat is formed on the surface of an intermediate transfer member in aninkjet printer, according to an embodiment of the present disclosure.

FIG. 4B is a side view of dried or semi-dried hydrophilic sacrificialcoating composition on the surface of the intermediate transfer memberafter a dryer removes a portion of a liquid carrier in the hydrophilicsacrificial coating composition, according to an embodiment of thepresent disclosure.

FIG. 4C is a side view of a portion of an aqueous ink image that isformed on the dried or semi-dried hydrophilic sacrificial coatingcomposition on the surface of the intermediate transfer member,according to an embodiment of the present disclosure.

FIG. 4D is a side view of a portion of the aqueous ink image that isformed on the dried hydrophilic sacrificial coating composition after adryer in the printer removes a portion of the water in the aqueous ink,according to an embodiment of the present disclosure.

FIG. 4E is a side view of a print medium that receives the aqueous inkimage and a portion of the dried layer of the hydrophilic sacrificialcoating composition after a transfix operation in the inkjet printer,according to an embodiment of the present disclosure.

It should be noted that some details of the figure have been simplifiedand are drawn to facilitate understanding of the embodiments rather thanto maintain strict structural accuracy, detail, and scale.

DESCRIPTION OF THE EMBODIMENTS

Reference will now be made in detail to embodiments of the presentteachings, examples of which are illustrated in the accompanyingdrawings. In the drawings, like reference numerals have been usedthroughout to designate identical elements. In the followingdescription, reference is made to the accompanying drawing that forms apart thereof, and in which is shown by way of illustration a specificexemplary embodiment in which the present teachings may be practiced.The following description is, therefore, merely exemplary.

As used herein, the terms “printer,” “printing device,” or “imagingdevice” generally refer to a device that produces an image on printmedia with aqueous ink and may encompass any such apparatus, such as adigital copier, bookmaking machine, facsimile machine, multi-functionmachine, or the like, which generates printed images for any purpose.Image data generally include information in electronic form which arerendered and used to operate the inkjet ejectors to form an ink image onthe print media. These data can include text, graphics, pictures, andthe like. The operation of producing images with colorants on printmedia, for example, graphics, text, photographs, and the like, isgenerally referred to herein as printing or marking. Aqueous inkjetprinters use inks that have a high percentage of water relative to theamount of colorant and/or solvent in the ink.

The term “printhead” as used herein refers to a component in the printerthat is configured with inkjet ejectors to eject ink drops onto an imagereceiving surface. A typical printhead includes a plurality of inkjetejectors that eject ink drops of one or more ink colors onto the imagereceiving surface in response to firing signals that operate actuatorsin the inkjet ejectors. The inkjets are arranged in an array of one ormore rows and columns. In some embodiments, the inkjets are arranged instaggered diagonal rows across a face of the printhead. Various printerembodiments include one or more printheads that form ink images on animage receiving surface. Some printer embodiments include a plurality ofprintheads arranged in a print zone. An image receiving surface, such asan intermediate imaging surface, moves past the printheads in a processdirection through the print zone. The inkjets in the printheads ejectink drops in rows in a cross-process direction, which is perpendicularto the process direction across the image receiving surface.

As used in this document, the term “aqueous ink” includes liquid inks inwhich colorant is in a solution, suspension or dispersion with a liquidvehicle that includes water and/or one or more liquid solvents. Theterms “liquid solvent” or more simply “solvent” are used broadly toinclude compounds that may dissolve colorants into a solution, or thatmay be a liquid that holds particles of colorant in a suspension ordispersion without dissolving the colorant.

As used herein, the term “hydrophilic” refers to any composition orcompound that attracts water molecules or other solvents used in aqueousink. As used herein, a reference to a hydrophilic composition refers toa liquid carrier that carries a hydrophilic agent. Examples of liquidcarriers include, but are not limited to, a liquid, such as water oralcohol, that carries a dispersion, suspension, or solution.

As used herein, a reference to a dried layer or dried coating refers toan arrangement of a hydrophilic compound after all or a substantialportion of the liquid carrier has been removed from the compositionthrough a drying process. As described in more detail below, an indirectinkjet printer forms a layer of a hydrophilic composition on a surfaceof an intermediate transfer member using a liquid carrier, such aswater, to apply a layer of the hydrophilic composition. The liquidcarrier is used as a mechanism to convey the hydrophilic composition toan image receiving surface to form a uniform layer of the hydrophiliccomposition on the image receiving surface.

An embodiment of the present disclosure is directed to a wet coatingcomposition for forming a sacrificial coating on an image transfermember in an aqueous ink imaging system. The wet coating composition ismade from ingredients comprising: a waxy starch; at least onepolycarboxylic acid cross-linking agent in an amount sufficient forcross-linking the waxy starch; at least one hygroscopic material; atleast one surfactant; and a liquid carrier. The coating optionallyincludes at least one polymer selected from the group consisting of i)polyvinyl alcohol and ii) a copolymer of vinyl alcohol and alkenemonomers.

In an embodiment, the waxy starch is a waxy maize starch. For example,the waxy maize starch can be a cationic waxy maize starch or anon-cationic waxy maize starch. Examples of cationic starch include acidtreated waxy maize starch, as described for example, in U.S. patentapplication Ser. No. 14/219,125, filed Mar. 19, 2014, in the name ofGuiqin Song et al., and entitled “WETTING ENHANCEMENT COATING ONINTERMEDIATE TRANSFER MEMBER (ITM) FOR AQUEOUS INKJET INTERMEDIATETRANSFER ARCHITECTURE,” the disclosure of which is incorporated hereinby reference in its entirety. Suitable non-cationic waxy maize starchesinclude acid depolymerized waxy starch, available from Cargill, Inc. asCALIBER® 180. The waxy starch may also be any other kind of waxy starchother than a waxy maize starch, such as a waxy rice starch, a waxycassava starch, a waxy potato starch, a waxy wheat starch and a waxybarley starch. The viscosity of the at least one waxy starch, such aswaxy maize starch, at about 25° C. may be less than about 1000 cps at astarch solid content of about 4%, such as less than about 700 cps, orless than 500 cps.

In certain embodiments disclosed herein, the at least one waxy starchmay be gelatinized. Starch gelatinization is a process that breaks downthe intermolecular bonds of starch molecules in the presence of waterand heat, allowing the hydrogen bonding sites (the hydroxyl hydrogen andoxygen) to engage more water. Therefore heating the at least one waxystarch in the presence of water irreversibly dissolves the starchgranule. For example, a waxy starch slurry can be prepared by mixingdeionized water with a desired amount of starch, such as a solid starchcontent of from about 1 weight percent to about 30 weight percent, basedon the total weight of the slurry. The starch slurry is gelatinized, orcooked out, either in a batch process or by a jet cooker. For batchprocess, the starch slurry can be heated to a temperature of, forexample, from about 93° C. to about 98° C., and kept at this temperaturefor about 15 minutes to about 60 minutes.

The waxy starch can be used in any suitable amount. In an embodiment,the weight percent of the starch in the wet sacrificial coating of thepresent disclosure ranges from about 0.5 weight percent to about 10weight percent, such as about 1 to about 8, or about 2 to about 6 weightpercent, based on the total weight of the wet sacrificial coatingcomposition.

As mentioned above, polyvinyl alcohol (PVOH) and copolymers thereof areoptionally included with the starch as part of the binder in thecompositions of the present disclosure. In an embodiment, the waxystarch and the at least one PVOH and/or PVOH co-polymer are respectivelyin a weight ratio ranging from about 2:1 to about 20:1, such as about3:1 to about 16:1, or about 4:1.

The PVOH and copolymers thereof can be selected from the groupconsisting of i) polyvinyl alcohol and ii) a copolymer of vinyl alcoholand alkene monomers. In an embodiment, the at least one polymer ispolyvinyl alcohol. In an embodiment, the at least one polymer is acopolymer of polyvinyl alcohol and alkene monomers. Examples of suitablepolyvinyl alcohol copolymers include poly(vinyl alcohol-co-ethylene). Inan embodiment, the poly(vinyl alcohol-co-ethylene) has an ethylenecontent ranging from about 5 mole % to about 30 mole %. Other examplesof polyvinyl copolymer include poly(acrylic acid)-poly(vinyl alcohol)copolymer, polyvinyl alcohol-acrylic acid-methyl methacrylate copolymerand poly(vinyl alcohol-co-aspartic acid) copolymer. One example of acommercially available PVOH is SELVOL™ PVOH 825, available from SekisuiSpecialty Chemicals of Dallas, Tex.

It is well known that PVOH can be manufactured by hydrolysis ofpolyvinyl acetate from, for example, partially hydrolyzed (87-89%),intermediate hydrolyzed (91-95%), fully hydrolyzed (98-98.8%) to superhydrolyzed (more than 99.3%). In an embodiment, the polyvinyl alcoholemployed in the compositions of the present disclosure has a hydrolysisdegree of at least 95% or higher, or at least 98% or 99.3% or higher.

The polyvinyl alcohol or copolymer thereof can have any suitablemolecular weight. In an embodiment, the weight average molecular weightranges from about 85,000 to about 186,000, such as from about 90,000 toabout 180,000, or from about 100,000 to about 170,000, or from about120,000 to about 150,000. Employing relatively high molecular weightPVOH can generate a strong thin film when combined with the starch andhelp to transfer the film onto the blanket. The loading of the PVOH isnot higher than 50%, since higher loading of high molecular weight PVOHcan significantly increase the viscosity and result in coating problems.

In an embodiment, the polyvinyl alcohol can have a suitable viscosityfor forming a sacrificial coating on an intermediate transfer member.For example, at about 4% by weight of the polyvinyl alcohol in asolution of deionized water, and at a temperature of 20° C., theviscosity can be at least 20 centipoises (“cps”), such as 25, 26 or 30cps or higher, where the % by weight of polyvinyl alcohol is relative tothe total weight of polyvinyl alcohol and water.

Polyvinyl alcohol is a hydrophilic polymer and has good water retentionproperties. As a hydrophilic polymer, the coating film formed frompolyvinyl alcohol can also exhibit good water retention properties,which can assist the ink spreading on the blanket. Because of itssuperior strength, coatings formulated with polyvinyl alcohol mayachieve a significant reduction in total solid loading level. This mayprovide substantial cost savings while providing a significantimprovement of the coating film performance. Polyvinyl alcohol andstarch based sacrificial coating compositions may have improvedmechanical properties and provide improved printer run-ability comparedto other known sacrificial coating compositions, such as, for example,improved ink skin transfer properties, particularly for long printingruns. Moreover, both polyvinyl alcohol and starch are consideredenvironmentally friendly, an important characteristic when used insacrificial coating compositions.

The at least one cross-linking agent can be any polycarboxylic acidcompound that is suitable for cross-linking the waxy starch and optionalpolyvinyl alcohol and/or copolymers thereof at a temperature and in aperiod of time so as to be useful in the printing processes of thepresent disclosure. The cross-linking agent can react with the hydroxylgroups or other moieties of the starch and/or PVOH to form the linkagesbetween molecules. In an embodiment, cross-linking agents that canprovide the desired degree of cross-linking at 180° C. or less, such asabout 160° C. or 150° C. or less, can be employed. In an embodiment, thecross-linking temperature ranges from about 80° C. to about 150° C. Thetime period for reaction may be in a range from about 0.1 second toabout 10 minutes, depending on the temperature applied.

Examples of suitable polycarboxylic acid cross-linking agents include atleast one compound selected from the group consisting of dicarboxylicacids, tricarboxylic acids, tetracarboxylic acids and water solublepolymeric carboxylic acids. In an embodiment, the compounds aredicarboxylic acids or tricarboxylic acids of formulae I or II:

where R¹ can be a saturated or unsaturated, linear, branched or cyclic,substituted or unsubstituted C₁ to C₂₀ carbon group optionallycontaining one or more heteroatoms. Examples of suitable R¹ groupsinclude C₁ to C₂₀ alkanediyl, C₁ to C₂₀ alkenediyl, C₁ to C₂₀ bisalkylene ether, C₁ to C₂₀ cycloalkylene and C₁ to C₂₀ arenediyl; and R²can be a saturated or unsaturated, linear, branched or cyclic,substituted or unsubstituted C₁ to C₂₀ carbon group, such as a C₁ to C₂₀alkanetriyl, C₁ to C₂₀ alkenetriyl, C₁ to C₂₀ cylcoalkanetriyl or C₁ toC₂₀ arenetriyl. The R¹ and R² groups can optionally be substituted withone or more functional groups, such as hydroxyl groups, carbonyl groupor amine groups.

Specific examples of suitable dicarboxylic acids of formula 1 includemalonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid,oleic acid dimer and sebacic acid. Specific examples of suitabletricarboxylic acids of formula 2 include pentane-1,3,5-tricarboxylicacid, benzene-1,3,5-tricarboxylic acid, isocitric acid, aconitic acid,propane-1,2,3-tricarboxylic acid, trimesic acid and citric acid. In anembodiment, the at least one tricarboxylic acid is citric acid.Polymeric carboxylic acids can also be employed. Specific examples ofsuitable water soluble polymeric carboxylic acids include poly(acrylicacid) and poly(methacrylic acid).

It is desirable for the starch and optional PVOH binders to remainsoluble in water for at least 24 hours. Addition of too muchcross-linking agent can potentially compromise the stability of thestarch solution, as well as the transfer efficiency of the image fromthe blanket to the substrate. Thus, suitable amounts of thecross-linking agents provide a desired balance between improvements inwater fastness and the potential detrimental effects to the stability ofthe starch solution and transfer efficiency of the image. Thecross-linking agent can be combined with the sacrificial coating at anypoint prior to deposition of the sacrificial coating. For example, thecross-linker can be combined with the sacrificial coating solution ashort time before loading the solution into the printer. Alternatively,an in line mixing process can be used with the cross-linking agent beingoptionally diluted into a vehicle compatible with the sacrificialcoating solution. In an embodiment, the starch and optional PVOH binderas well as humectant solution are mixed with cross-linker just beforethe application on the underlying ITM surface.

The loading of the cross-linking agent can be varied and depends on thetype of cross-linker. Example amounts can range from about 2% to about30% by weight, such as from about 2% to about 10% by weight, based onthe total loading of the binders. One, two, three or more of any of theabove cross-linkers can be employed.

The chemical structure of the starch and optional polyvinyl alcoholcontaining coating can be tailored to fine-tune the wettability andrelease characteristics of the sacrificial coating from the underlyingITM surface. This can be accomplished by employing one or morehygroscopic materials and one or more surfactants in the coatingcomposition. However, employing a starch-PVOH based sacrificial coatingwith hygroscopic materials can adversely affect the water fastness ofinkjet prints. While the use of the hygroscopic materials in combinationwith the starch binder may exacerbate problems with water fastness, theinventors have found that the addition of the cross-linking agentsdescribed above can minimize and in many cases eliminate the problem.

Any suitable hygroscopic material can be employed in the sacrificialcoating compositions of the present disclosure. Hygroscopic materialscan include substances capable of absorbing water from theirsurroundings, such as humectants. In an embodiment, the hygroscopicmaterial can be a compound that is also functionalized as a plasticizer.In an embodiment, the at least one hygroscopic material is selected fromthe group consisting of glycerol, sorbitol or glycols such aspolyethylene glycol, and mixtures thereof. A single hygroscopic materialcan be used. Alternatively, multiple hygroscopic materials, such as two,three or more hygroscopic materials, can be used.

Any suitable surfactants can be employed. Examples of suitablesurfactants include anionic surfactants, cationic surfactants, non-ionicsurfactants and mixtures thereof. The non-ionic surfactants can have anHLB value ranging from about 4 to about 14. A single surfactant can beused. Alternatively, multiple surfactants, such as two, three or moresurfactants, can be used. For example, the mixture of a low HLBnon-ionic surfactant with a value from about 4 to about 8 and a high HLBnon-ionic surfactant with value from about 10 to about 14 demonstratesgood wetting performance. In an embodiment, the at least one surfactantis sodium lauryl sulfate.

The wet compositions of the present disclosure include a liquid carrier.The liquid carrier can be an aqueous based carrier, such as a carriercomprising at least 50% by weight water, such as 90% or 95% by weight ormore water, such as 100%. Other ingredients that can be included as partof the aqueous based carrier system include organic solvents, such asketones. An example of a ketone solvent is 2-Pyrrolidinone, which canpotentially replace some loading of the glycerol. Other organic solventsthat can be used in addition to or in place of 2-Pyrrolidinone includeterpineol; dimethylsulfoxide; N-methylpyrrolidone;1,3-dimethyl-2-imidazolidinone; 1,3-dimethyl-3,4,5,6-tetrahydro-2pyrimidinone; dimethylpropylene urea; isopropanol, MEK (methyl ethylketone) and mixtures thereof. The organic solvents can have benefits,such as to improve film forming property, control drying characteristicsand control wetting property of the semi-dry sacrificial layer. In anembodiment, the aqueous based carrier is 100% water.

Initially, the sacrificial coating composition is applied to theintermediate transfer member (“ITM”), where it is semi-dried or dried toform a film. The coating can have a higher surface energy and/or be morehydrophilic than the base ITM, which is usually a material with lowsurface free energy, such as, for example, a polysiloxane, such aspolydimethylsiloxane or other silicone rubber material, fluorosilicone,TEFLON, polyimide or combinations thereof.

In an embodiment, the sacrificial coating is made by mixing theingredients comprising: a waxy starch; at least one polycarboxylic acidcross-linking agent in an amount sufficient for cross-linking the waxystarch; at least one hygroscopic material; at least one surfactant; aliquid carrier and optionally at least one polymer selected from thegroup consisting of i) polyvinyl alcohol and ii) a copolymer of vinylalcohol and alkene monomers.

In addition to the ingredients discussed above, the mixture can includeother ingredients, such biocides. Example biocides include ACTICIDES®CT, ACTICIDES® LA 1209 and ACTICIDES® MBS in any suitable concentration,such as from about 0.1 weight percent to about 2 weight percent.

The ingredients of the sacrificial coating can be mixed in any suitablemanner to form a composition that can be coated onto the intermediatetransfer member. The ingredients can be mixed in any suitable amounts.For example, the waxy starch can be added in an amount of from about 0.5to about 10 weight percent, or from about 2 to about 8, or from about 5to about 7 weight percent based upon the total weight of the coatingmixture. The optional polyvinyl alcohol or vinyl alcohol copolymer canbe added in an amount of from about 0 to about 5% by weight, or fromabout 0.5 to about 4% by weight, or from about 1 to about 3% by weight,based upon the total weight of the coating mixture. The surfactants canbe present in an amount of from about 0.01 to about 4% by weight, orfrom about 0.05 to about 2% by weight, or from about 0.08 to about 1% byweight, based upon the total weight of the coating mixture. Thehygroscopic material can be present in an amount of from about 0.5 toabout 30% by weight, or from about 2 to about 25% by weight, or fromabout 4 to about 20% by weight, or about 10 to about 15% by weight,based upon the total weight of the coating mixture.

The compositions of the present disclosure can be used to form asacrificial coating over any suitable substrate. Any suitable coatingmethod can be employed, including, but not limited to, dip coating,spray coating, spin coating, flow coating, stamp printing, die extrusioncoatings, flexo and gravure coating and/or blade techniques. Inexemplary embodiments, suitable methods can be employed to coat theliquid sacrificial coating composition on an intermediate transfermember, such as, for example, use of an anilox roller, as shown in FIG.2; or an air atomization device, such as an air brush or an automatedair/liquid sprayer can be used for spray coating. In another example, aprogrammable dispenser can be used to apply the coating material toconduct a flow coating.

As described above, the sacrificial coating is first applied or disposedas a wet coating on the intermediate transfer member. A drying or curingprocess can then be employed. In embodiments, the wet coating can beheated at an appropriate temperature for the drying and curing,depending on the material or process used. For example, the wet coatingcan be heated to a temperature ranging from about 30° C. to about 200°C. for about 0.01 to about 100 seconds or from about 0.1 second to about60 seconds. Also, the speed of air flow can be adjusted during thedrying process to accelerate drying at low temperature. In embodiments,after the drying and curing process, the sacrificial coating can have athickness ranging from about 0.02 micrometer to about 10 micrometers, orfrom about 0.02 micrometer to about 5 micrometers, or from about 0.05micrometer to about 1 micrometers.

In an embodiment, the sacrificial coating can cover a portion of a majorsurface of the intermediate transfer member. The major outer surface ofthe intermediate transfer member can comprise, for example,polysiloxanes, fluoro-silicones, fluoropolymers such as VITON or TEFLONand the like.

It has been found that the sacrificial coating overcomes the wet imagequality problem discussed above by providing an ink wetting surface onthe intermediate transfer member. The coatings may also improve theimage cohesion significantly to enable excellent image transfer.

FIG. 1 illustrates a high-speed aqueous ink image producing machine orprinter 10. As illustrated, the printer 10 is an indirect printer thatforms an ink image on a surface of a blanket 21 mounted about anintermediate rotating member 12 and then transfers the ink image tomedia passing through a nip 18 formed between the blanket 21 and thetransfix roller 19. The surface 14 of the blanket 21 is referred to asthe image receiving surface of the blanket 21 and the rotating member 12since the surface 14 receives a hydrophilic composition and the aqueousink images that are transfixed to print media during a printing process.A print cycle is now described with reference to the printer 10. As usedin this document, “print cycle” refers to the operations of a printer toprepare an imaging surface for printing, ejection of the ink onto theprepared surface, treatment of the ink on the imaging surface tostabilize and prepare the image for transfer to media, and transfer ofthe image from the imaging surface to the media.

The printer 10 includes a frame 11 that supports directly or indirectlyoperating subsystems and components, which are described below. Theprinter 10 includes an intermediate transfer member, which isillustrated as rotating imaging drum 12 in FIG. 1, but can also haveother suitable configurations, such as a supported endless belt. Theimaging drum 12 has an outer blanket 21 mounted about the circumferenceof the drum 12. The blanket moves in a direction 16 as the member 12rotates. A transfix roller 19 rotatable in the direction 17 is loadedagainst the surface of blanket 21 to form a transfix nip 18, withinwhich ink images formed on the surface of blanket 21 are transfixed ontoa print medium 49. In some embodiments, a heater in the drum 12 (notshown) or in another location of the printer heats the image receivingsurface 14 on the blanket 21 to a temperature in a range of, forexample, approximately 50° C. to approximately 70° C. The elevatedtemperature promotes partial drying of the liquid carrier that is usedto deposit the hydrophilic composition and of the water in the aqueousink drops that are deposited on the image receiving surface 14.

The blanket is formed of a material having a relatively low surfaceenergy to facilitate transfer of the ink image from the surface of theblanket 21 to the print medium 49 in the nip 18. Such materials includepolysiloxanes, fluoro-silicones, fluoropolymers such as VITON or TEFLONand the like. A surface maintenance unit (SMU) 92 removes residual inkleft on the surface of the blanket 21 after the ink images aretransferred to the print medium 49. The low energy surface of theblanket is not necessarily designed to aid in the formation of goodquality ink images, at least because such surfaces do not spread inkdrops as well as high energy surfaces.

In an embodiment more clearly depicted in FIG. 2, the SMU 92 includes acoating applicator, such as a donor roller 404, which is partiallysubmerged in a reservoir 408 that holds the wet sacrificial coatingcompositions of the present disclosure. The donor roller 404 rotates inresponse to the movement of the image receiving surface 14 in theprocess direction. The donor roller 404 draws the liquid sacrificialcoating composition from the reservoir 408 and deposits a layer of thecomposition on the image receiving surface 14. As described below, thesacrificial coating composition is deposited as a uniform layer havingany desired thickness. Examples include thicknesses ranging from about0.1 μm to about 10 μm. The SMU 92 deposits the sacrificial coatingcomposition on the image receiving surface 14. After a drying process,the dried sacrificial coating substantially covers the image receivingsurface 14 before the printer ejects ink drops during a print process.In some illustrative embodiments, the donor roller 404 is an aniloxroller or an elastomeric roller made of a material, such as rubber. TheSMU 92 can be operatively connected to a controller 80, described inmore detail below, to enable the controller to operate the donor roller,as well as a metering blade and a cleaning blade, which may respectivelyfunction to deposit and distribute the coating material onto the surfaceof the blanket and to remove un-transferred ink and any sacrificialcoating residue from the surface of the blanket 21.

Referring back to FIG. 1, the printer 10 includes a dryer 96 that emitsheat and optionally directs an air flow toward the wet sacrificialcoating composition that is applied to the image receiving surface 14.The dryer 96 facilitates the evaporation of at least a portion of theliquid carrier from the wet sacrificial coating composition to leave adried layer on the image receiving surface 14 before the intermediatetransfer member passes the printhead modules 34A-34D to receive theaqueous printed image.

The printer 10 can include an optical sensor 94A, also known as animage-on-drum (“IOD”) sensor, which is configured to detect lightreflected from the blanket surface 14 and the sacrificial coatingapplied to the blanket surface as the member 12 rotates past the sensor.The optical sensor 94A includes a linear array of individual opticaldetectors that are arranged in the cross-process direction across theblanket 21. The optical sensor 94A generates digital image datacorresponding to light that is reflected from the blanket surface 14 andthe sacrificial coating. The optical sensor 94A generates a series ofrows of image data, which are referred to as “scanlines,” as theintermediate transfer member 12 rotates the blanket 21 in the direction16 past the optical sensor 94A. In one embodiment, each optical detectorin the optical sensor 94A further comprises three sensing elements thatare sensitive to wavelengths of light corresponding to red, green, andblue (RGB) reflected light colors. Alternatively, the optical sensor 94Aincludes illumination sources that shine red, green, and blue light or,in another embodiment, the sensor 94A has an illumination source thatshines white light onto the surface of blanket 21 and white lightdetectors are used. The optical sensor 94A shines complementary colorsof light onto the image receiving surface to enable detection ofdifferent ink colors using the photodetectors. The image data generatedby the optical sensor 94A can be analyzed by the controller 80 or otherprocessor in the printer 10 to identify the thickness of the sacrificialcoating on the blanket and the area coverage. The thickness and coveragecan be identified from either specular or diffuse light reflection fromthe blanket surface and/or coating. Other optical sensors, such as 94B,94C, and 94D, are similarly configured and can be located in differentlocations around the blanket 21 to identify and evaluate otherparameters in the printing process, such as missing or inoperativeinkjets and ink image formation prior to image drying (94B), ink imagetreatment for image transfer (94C), and the efficiency of the ink imagetransfer (94D). Alternatively, some embodiments can include an opticalsensor to generate additional data that can be used for evaluation ofthe image quality on the media (94E).

The printer 10 includes an airflow management system 100, whichgenerates and controls a flow of air through the print zone. The airflowmanagement system 100 includes a printhead air supply 104 and aprinthead air return 108. The printhead air supply 104 and return 108are operatively connected to the controller 80 or some other processorin the printer 10 to enable the controller to manage the air flowingthrough the print zone. This regulation of the air flow can be throughthe print zone as a whole or about one or more printhead arrays. Theregulation of the air flow helps prevent evaporated solvents and waterin the ink from condensing on the printhead and helps attenuate heat inthe print zone to reduce the likelihood that ink dries in the inkjets,which can clog the inkjets. The airflow management system 100 can alsoinclude sensors to detect humidity and temperature in the print zone toenable more precise control of the temperature, flow, and humidity ofthe air supply 104 and return 108 to ensure optimum conditions withinthe print zone. Controller 80 or some other processor in the printer 10can also enable control of the system 100 with reference to ink coveragein an image area or even to time the operation of the system 100 so aironly flows through the print zone when an image is not being printed.

The high-speed aqueous ink printer 10 also includes an aqueous inksupply and delivery subsystem 20 that has at least one source 22 of onecolor of aqueous ink. Since the illustrated printer 10 is a multicolorimage producing machine, the ink delivery system 20 includes, forexample, four (4) sources 22, 24, 26, 28, representing four (4)different colors CYMK (cyan, yellow, magenta, black) of aqueous inks. Inthe embodiment of FIG. 1, the printhead system 30 includes a printheadsupport 32, which provides support for a plurality of printhead modules,also known as print box units, 34A through 34D. Each printhead module34A-34D effectively extends across the width of the blanket and ejectsink drops onto the surface 14 of the blanket 21. A printhead module caninclude a single printhead or a plurality of printheads configured in astaggered arrangement. Each printhead module is operatively connected toa frame (not shown) and aligned to eject the ink drops to form an inkimage on the coating on the blanket surface 14. The printhead modules34A-34D can include associated electronics, ink reservoirs, and inkconduits to supply ink to the one or more printheads. In the illustratedembodiment, conduits (not shown) operatively connect the sources 22, 24,26, and 28 to the printhead modules 34A-34D to provide a supply of inkto the one or more printheads in the modules. As is generally familiar,each of the one or more printheads in a printhead module can eject asingle color of ink. In other embodiments, the printheads can beconfigured to eject two or more colors of ink. For example, printheadsin modules 34A and 34B can eject cyan and magenta ink, while printheadsin modules 34C and 34D can eject yellow and black ink. The printheads inthe illustrated modules are arranged in two arrays that are offset, orstaggered, with respect to one another to enable a continuous coverageof printing across the cross process width of the printing zone.Although the printer 10 includes four printhead modules 34A-34D, each ofwhich has two arrays of printheads, alternative configurations include adifferent number of printhead modules or arrays within a module.

After the printed image on the blanket surface 14 exits the print zone,the image passes under an image dryer 130. The image dryer 130 includesa heater, such as a radiant infrared, radiant near infrared and/or aforced hot air convection heater 134, a dryer 136, which is illustratedas a heated air source 136, and air returns 138A and 138B. The infraredheater 134 applies infrared heat to the printed image on the surface 14of the blanket 21 to evaporate water or solvent in the ink. The heatedair source 136 directs heated air over the ink to supplement theevaporation of the water or solvent from the ink. In one embodiment, thedryer 136 is a heated air source with the same design as the dryer 96.While the dryer 96 is positioned along the process direction to dry thehydrophilic composition, the dryer 136 is positioned along the processdirection after the printhead modules 34A-34D to at least partially drythe aqueous ink on the image receiving surface 14. The air is thencollected and evacuated by air returns 138A and 138B to reduce theinterference of the air flow with other components in the printing area.

As further shown, the printer 10 includes a print medium supply andhandling system 40 that stores, for example, one or more stacks of paperprint mediums of various sizes. The print medium supply and handlingsystem 40, for example, includes sheet or substrate supply sources 42,44, 46, and 48. In the embodiment of printer 10, the supply source 48 isa high capacity paper supply or feeder for storing and supplying imagereceiving substrates in the form of cut print mediums 49, for example.The print medium supply and handling system 40 also includes a substratehandling and transport system 50 that has a media pre-conditionerassembly 52 and a media post-conditioner assembly 54. The printer 10includes an optional fusing device 60 to apply additional heat andpressure to the print medium after the print medium passes through thetransfix nip 18. In the embodiment of FIG. 1, the printer 10 includes anoriginal document feeder 70 that has a document holding tray 72,document sheet feeding and retrieval devices 74, and a document exposureand scanning system 76.

Operation and control of the various subsystems, components andfunctions of the machine or printer 10 are performed with the aid of acontroller or electronic subsystem (ESS) 80. The ESS or controller 80 isoperably connected to, for example, the intermediate transfer member 12,the printhead modules 34A-34D (and thus the printheads), the substratesupply and handling system 40, the substrate handling and transportsystem 50, and, in some embodiments, the one or more optical sensors94A-94E. The ESS or controller 80, for example, is a self-contained,dedicated mini-computer having a central processor unit (CPU) 82 withelectronic storage 84, and a display or user interface (UI) 86. The ESSor controller 80, for example, includes a sensor input and controlcircuit 88 as well as a pixel placement and control circuit 89. Inaddition, the CPU 82 reads, captures, prepares and manages the imagedata flow between image input sources, such as the scanning system 76,or an online or a work station connection 90, and the printhead modules34A-34D. As such, the ESS or controller 80 is the main multi-taskingprocessor for operating and controlling all of the other machinesubsystems and functions, including the printing process discussedbelow.

The controller 80 can be implemented with general or specializedprogrammable processors that execute programmed instructions. Theinstructions and data required to perform the programmed functions canbe stored in memory associated with the processors or controllers. Theprocessors, their memories, and interface circuitry configure thecontrollers to perform the operations described below. These componentscan be provided on a printed circuit card or provided as a circuit in anapplication specific integrated circuit (ASIC). Each of the circuits canbe implemented with a separate processor or multiple circuits can beimplemented on the same processor. Alternatively, the circuits can beimplemented with discrete components or circuits provided in very largescale integrated (VLSI) circuits. Also, the circuits described hereincan be implemented with a combination of processors, ASICs, discretecomponents, or VLSI circuits.

Although the printer 10 in FIG. 1 is described as having a blanket 21mounted about an intermediate rotating member 12, other configurationsof an image receiving surface can be used. For example, the intermediaterotating member can have a surface integrated into its circumferencethat enables an aqueous ink image to be formed on the surface.Alternatively, a blanket is configured as an endless rotating belt forformation of an aqueous image. Other variations of these structures canbe configured for this purpose. As used in this document, the term“intermediate imaging surface” includes these various configurations.

Once an image or images have been formed on the blanket and coatingunder control of the controller 80, the illustrated inkjet printer 10operates components within the printer to perform a process fortransferring and fixing the image or images from the blanket surface 14to media. In the printer 10, the controller 80 operates actuators todrive one or more of the rollers 64 in the media transport system 50 tomove the print medium 49 in the process direction P to a positionadjacent the transfix roller 19 and then through the transfix nip 18between the transfix roller 19 and the blanket 21. The transfix roller19 applies pressure against the back side of the print medium 49 inorder to press the front side of the print medium 49 against the blanket21. Although the transfix roller 19 can also be heated, in the exemplaryembodiment of FIG. 1 the transfix roller 19 is unheated. Instead, thepre-heater assembly 52 for the print medium 49 is provided in the mediapath leading to the nip. The pre-conditioner assembly 52 conditions theprint medium 49 to a predetermined temperature that aids in thetransferring of the image to the media, thus simplifying the design ofthe transfix roller. The pressure produced by the transfix roller 19 onthe back side of the heated print medium 49 facilitates the transfixing(transfer and fusing) of the image from the intermediate transfer member12 onto the print medium 49. The rotation or rolling of both theintermediate transfer member 12 and transfix roller 19 not onlytransfixes the images onto the print medium 49, but also assists intransporting the print medium 49 through the nip. The intermediatetransfer member 12 continues to rotate to enable the printing process tobe repeated.

After the intermediate transfer member 12 moves through the transfix nip18, the image receiving surface passes a cleaning unit that removesresidual portions of the sacrificial coating and small amounts ofresidual ink from the image receiving surface 14. In the printer 10, thecleaning unit is embodied as a cleaning blade 95 that engages the imagereceiving surface 14. The blade 95 is formed from a material that wipesthe image receiving surface 14 without causing damage to the blanket 21.For example, the cleaning blade 95 is formed from a flexible polymermaterial in the printer 10. As depicted below in FIG. 1, anotherembodiment has a cleaning unit that includes a roller or other memberthat applies a mixture of water and detergent to remove residualmaterials from the image receiving surface 14 after the intermediatetransfer member moves through the transfix nip 18. As used herein, theterm “detergent” or cleaning agent refers to any surfactant, solvent, orother chemical compound that is suitable for removing any sacrificialcoating and any residual ink that may remain on the image receivingsurface from the image receiving surface. One example of a suitabledetergent is sodium stearate, which is a compound commonly used in soap.Another example is IPA, which is common solvent that is very effectiveto remove ink residues from the image receiving surface. In anembodiment, no residue of the sacrificial coating layer remains on theITM after transferring the ink and sacrificial layer, in which casecleaning of the ITM to remove residual sacrificial coating may not be anissue.

FIG. 3 depicts a process 700 for operating an aqueous indirect inkjetprinter using a sacrificial coating composition, as described herein, toform a dried coating on an image receiving surface of an intermediatetransfer member prior to ejecting liquid ink drops onto the dried layer.In the discussion below, a reference to the process 700 performing anaction or function refers to a controller, such as the controller 80 inthe printer 10, executing stored programmed instructions to perform theaction or function in conjunction with other components of the printer.The process 700 is described in conjunction with FIG. 1 showing theprinter 10, and FIG. 4A-FIG. 4E showing the blanket and coatings, forillustrative purposes. The sacrificial coatings and processes ofemploying these coatings are not limited to use with printer 10, but canpotentially be employed with any inkjet printer comprising anintermediate transfer member, as would be readily understood by one ofordinary skill in the art.

Process 700 begins as the printer applies a sacrificial layer of a wetcoating composition with a liquid carrier to the image receiving surfaceof the intermediate transfer member (block 704). In the printer 10, thedrum 12 and blanket 21 move in the process direction along the indicatedcircular direction 16 during the process 700 to receive the sacrificialcoating composition.

In an embodiment, the liquid carrier is water or another liquid, such asalcohol or any of the other liquid carriers described herein for use inthe wet coating composition, which partially evaporates from the imagereceiving surface and leaves a dried layer on the image receivingsurface. In FIG. 4A, the surface of the intermediate transfer member 504is covered with the sacrificial coating composition 508. The SMU 92deposits the sacrificial coating composition on the image receivingsurface 14 of the blanket 21 to form a uniform hydrophilic coating. Agreater coating thickness of the sacrificial coating composition enablesformation of a uniform layer that completely covers the image receivingsurface, but the increased volume of liquid carrier in the thickercoating requires additional drying time or larger dryers to remove theliquid carrier to form a dried layer. Thinner coatings of thesacrificial coating composition require the removal of a smaller volumeof the liquid carrier to form the dried layer, but if the sacrificialcoating is too thin, then the coating may not fully cover the imagereceiving surface. In certain embodiments the sacrificial coatingcomposition with the liquid carrier is applied at a thickness of betweenapproximately 1 μm and 10 μm

Process 700 continues as a dryer in the printer dries the sacrificialcoating composition to remove at least a portion of the liquid carrierand to form a dried layer on the image receiving surface (block 708). Inthe printer 10 the dryer 96 applies radiant heat and optionally includesa fan to circulate air onto the image receiving surface of the drum 12.FIG. 4B depicts the dried layer 512. The dryer 96 removes a portion ofthe liquid carrier, which decreases the thickness of the layer of driedlayer that is formed on the image receiving surface. In the printer 10the thickness of the dried layer 512 can be any suitable desiredthickness. Example thicknesses range from about 0.1 μm to about 3 μm indifferent embodiments, and in certain specific embodiments from about0.1 to about 0.5 μm

The dried sacrificial coating 512 is also referred to as a “skin” layer.The dried sacrificial coating 512 has a uniform thickness that coverssubstantially all of the portion of the image receiving surface thatreceives aqueous ink during a printing process. As described above,while the sacrificial coating with the liquid carrier includessolutions, suspension, or dispersion of the sacrificial coating materialin a liquid carrier, the dried sacrificial coating 512 covers the imagereceiving surface of intermediate transfer member 504. The driedsacrificial coating 512 has a comparatively high level of adhesion tothe image receiving surface of intermediate transfer member 504, and acomparatively low level of adhesion to a print medium that contacts thedried layer 512. As described in more detail below, when aqueous inkdrops are ejected onto portions of the dried layer 512, a portion of thewater and other solvents in the aqueous ink permeates the dried layer512.

Process 700 continues as the image receiving surface with thehydrophilic skin layer moves past one or more printheads that ejectaqueous ink drops onto the dried layer and the image receiving surfaceto form a latent aqueous printed image (block 712). The printheadmodules 34A-34D in the printer 10 eject ink drops in the CMYK colors toform the printed image.

The sacrificial coating 512 is substantially impermeable to thecolorants in the ink 524, and the colorants remain on the surface of thedried layer 512 where the aqueous ink spreads. The spread of the liquidink enables neighboring aqueous ink drops to merge together on the imagereceiving surface instead of beading into individual droplets as occursin traditional low-surface energy image receiving surfaces.

Referring again to FIG. 3, the process 700 continues with a partialdrying process of the aqueous ink on the intermediate transfer member(block 716). The drying process removes a portion of the water from theaqueous ink and the sacrificial coating, also referred to as the skinlayer, on the intermediate transfer member so that the amount of waterthat is transferred to a print medium in the printer does not producecockling or other deformations of the print medium. In the printer 10,the heated air source 136 directs heated air toward the image receivingsurface 14 to dry the printed aqueous ink image. In some embodiments,the intermediate transfer member and blanket are heated to an elevatedtemperature to promote evaporation of liquid from the ink. For example,in the printer 10, the imaging drum 12 and blanket 21 are heated to atemperature of 50° C. to 70° C. to enable partial drying of the ink onthe dried sacrificial layer during the printing process. As depicted inFIG. 4D, the drying process forms a partially dried aqueous ink 532 thatretains a reduced amount of water compared to the freshly printedaqueous ink image of FIG. 4C.

The drying process increases the viscosity of the aqueous ink, whichchanges the consistency of the aqueous ink from a low-viscosity liquidto a higher viscosity tacky material. The drying process also reducesthe thickness of the ink 532. In an embodiment, the drying processremoves sufficient water so that the ink contains less that 20% water byweight, such as less than 5% water, or even less than 2% water, byweight of the partially dried ink (the ink after drying but beforetransfer to the print medium).

Process 700 continues as the printer transfixes the latent aqueous inkimage from the image receiving surface to a print medium, such as asheet of paper (block 720). In the printer 10, the image receivingsurface 14 of the drum 12 engages the transfix roller 19 to form a nip18. A print medium, such as a sheet of paper, moves through the nipbetween the drum 12 and the transfix roller 19. The pressure in the niptransfers the aqueous ink image and a portion of the dried sacrificiallayer to the print medium. After passing through the transfix nip 18,the print medium carries the printed aqueous ink image. As depicted inFIG. 4E, a print medium 536 carries a printed aqueous ink image 532 withthe sacrificial coating 512 covering the ink image 532 on the surface ofthe print medium 536. The sacrificial coating 512 provides protection tothe aqueous ink image from scratches or other physical damage while theaqueous ink image 532 dries on the print medium 536.

During process 700, the printer cleans any residual portions of thesacrificial coating 512 that may remain on the image receiving surfaceafter the transfixing operation (block 724). In one embodiment, acleaning system uses, for example, a combination of water and adetergent with mechanical agitation on the image receiving surface toremove the residual portions of the sacrificial coating 512 from thesurface of the drum 12. In the printer 10, a cleaning blade 95, whichcan be used in conjunction with water, engages the blanket 21 to removeany residual sacrificial coating 512 from the image receiving surface14. The cleaning blade 95 is, for example, a polymer blade that wipesresidual portions of the sacrificial coating 512 from the blanket 21.

During a printing operation, process 700 returns to the processingdescribed above with reference to block 704 to apply the hydrophiliccomposition to the image receiving surface, print additional aqueous inkimages, and transfix the aqueous ink images to print media foradditional printed pages in the print process. The illustrativeembodiment of the printer 10 operates in a “single pass” mode that formsthe dried layer, prints the aqueous ink image and transfixes the aqueousink image to a print medium in a single rotation or circuit of theintermediate transfer member. In alternative embodiments, an inkjetemploys a multi-pass configuration where the image receiving surfacecompletes two or more rotations or circuits to form the dried layer andreceive the aqueous ink image prior to transfixing the printed image tothe print medium.

In some embodiments of the process 700, the printer forms printed imagesusing a single layer of ink such as the ink 524 that is depicted in FIG.4C. In the printer 10, however, the multiple printhead modules enablethe printer to form printed images with multiple colors of ink. In otherembodiments of the process 700, the printer forms images using multipleink colors. In some regions of the printed image, multiple colors of inkmay overlap in the same area on the image receiving surface, formingmultiple ink layers on the hydrophilic composition layer. The methodsteps in FIG. 3 can be applied to the multiple ink layer circumstancewith similar results.

EXAMPLES Example 1: Sacrificial Coating Compositions

A drop of 5% by weight solution of citric acid was added to an Oceanshalf tone print and dried at 120° C. The area of the print treated withcitric acid showed significantly improved water fastness compared tonon-treated areas, areas that had been treated with a drop of water anddried, and areas that had been treated with a drop of 5% by weight Boraxsolution and dried.

Notwithstanding that the numerical ranges and parameters setting forththe broad scope of the disclosure are approximations, the numericalvalues set forth in the specific examples are reported as precisely aspossible. Any numerical value, however, inherently contains certainerrors necessarily resulting from the standard deviation found in theirrespective testing measurements. Moreover, all ranges disclosed hereinare to be understood to encompass any and all sub-ranges subsumedtherein.

While the present teachings have been illustrated with respect to one ormore implementations, alterations and/or modifications can be made tothe illustrated examples without departing from the spirit and scope ofthe appended claims. In addition, while a particular feature of thepresent teachings may have been disclosed with respect to only one ofseveral implementations, such feature may be combined with one or moreother features of the other implementations as may be desired andadvantageous for any given or particular function. Furthermore, to theextent that the terms “including,” “includes,” “having,” “has,” “with,”or variants thereof are used in either the detailed description and theclaims, such terms are intended to be inclusive in a manner similar tothe term “comprising.” Further, in the discussion and claims herein, theterm “about” indicates that the value listed may be somewhat altered, aslong as the alteration does not result in nonconformance of the processor structure to the illustrated embodiment. Finally, “exemplary”indicates the description is used as an example, rather than implyingthat it is an ideal.

It will be appreciated that variants of the above-disclosed and otherfeatures and functions, or alternatives thereof, may be combined intomany other different systems or applications. Various presentlyunforeseen or unanticipated alternatives, modifications, variations, orimprovements therein may be subsequently made by those skilled in theart which are also intended to be encompasses by the following claims.

What is claimed is:
 1. A sacrificial coating on an intermediate transfermember of an aqueous ink imaging system, the sacrificial coating madefrom ingredients comprising: a waxy starch; at least one polycarboxylicacid cross-linking agent; at least one hygroscopic material; and atleast one surfactant.
 2. The sacrificial coating of claim 1, wherein thewaxy starch comprises at least one starch selected from the groupconsisting of a waxy maize starch, a waxy rice starch, a waxy cassavastarch, a waxy potato starch, a waxy wheat starch and a waxy barleystarch.
 3. The sacrificial coating of claim 1, wherein the at least onepolycarboxylic acid is selected from the group consisting ofdicarboxylic acids and tricarboxylic acids.
 4. The sacrificial coatingof claim 1, wherein the at least one polycarboxylic acid is citric acid.5. The sacrificial coating of claim 1, wherein the at least onepolycarboxylic acid is a water soluble polymeric carboxylic acid.
 6. Thesacrificial coating of claim 1, wherein the sacrificial coating furthercomprising at least one polymer selected from the group consisting of i)polyvinyl alcohol and ii) a copolymer of vinyl alcohol and alkenemonomers.